The present work addresses the competition between dislocation plasticity and stress-induced martensitic transformations in crack affected regions of a pseudoelastic NiTi miniature compact tension specimen. For this purpose X-ray line profile analysis was performed after fracture to identify dislocation densities and remnant martensite volume fractions in regions along the crack path. Special emphasis was placed on characterizing sub fracture surface zones to obtain depth profiles. The stress affected zone in front of the crack-tip is interpreted in terms of a true plastic zone associated with dislocation plasticity and a pseudoelastic zone where stress-induced martensite can form. On unloading, most of the stress-induced martensite transforms back to austenite but a fraction of it is stabilized by dislocations in both, the irreversible martensite and the surrounding austenite phase. The largest volume fraction of the irreversible or remnant martensite along with the highest density of dislocations in this phase was found close to the primary crack-tip. With increasing distance from the primary crack-tip both, the dislocation density and the volume fraction of irreversible martensite decrease to lower values.

SnSb nanoparticles are dispersed in carbon nanofibers by electrospinning technology and different SnSb precursors, including Sn0.92Sb0.08O2.04 nanoparticles, Sn(CH3COO)2/Sb(CH3COO)3, and SnCl4·5H2O/SbCl3, are used to tune the morphology of the resultant SnSb/C nanofibers. Porous SnSb/C nanofibers are formed during carbonization Sn0.92Sb0.08O2.04 nanoparticles and Sn(CH3COO)2/Sb(CH3COO)3 are used as precursors of SnSb, while solid nanofibers are observed with SnCl4·5H2O/SbCl3 as the precursor indicating the formation mechanism is closely related to the properties of SnSb precursors. Excellent cycling preference (99% capacity retention after 200 cycles) and high coulombic efficiency (above 99% after 10 cycles) are obtained for the SnSb/C nanofibers using Sn0.92Sb0.08O2.04 as precursor, due to its high surface area and stable SnSb/C structure. It is demonstrated that the uniquely designed composite nanofiber structure with excellent lithium storage performance can be realized simply by selecting precursors with appropriate dissolution and decomposition properties.

Four 9Cr2WVTa deposited metals with different titanium contents were studied to reveal the role of minor elements titanium, which guide for the design of welding consumables for reduced activation ferritic/martensitic steel and meet for the requirements of accelerator driven systems-lead fusion reactors. The microstructural evolution of 9Cr2WVTa deposited metals was analyzed and discussed. Results show that the surface layer of 9Cr2WVTa deposited metal exhibits the columnar structure and the δ-ferrite is seen as a film distributed along the martensite lath. The microstructures are uniform in the middle of the deposited metal and exhibit the equiaxed structure. The fine stripe δ-ferrite decorates along the prior austenite grain boundaries and therefore, refines the grain size. The primary blocky Ti-enriched particles are the main factor affecting the mechanical properties for the 9Cr2WVTa deposited metal. The 9Cr2WVTa deposited metals obtain good mechanical properties when the titanium content does not exceed 0.08 wt%.

2-(3,4 epoxycyclohexyl)ethyltrimethoxysilane (EETMS)/3-glycidoxypropyltrimethoxysilane (GPTMS) mediated, in situ synthesis of functional palladium (Pd) nanocomposites over the graphene oxide (GO) surface is reported. The prepared nanocomposites viz, Pd/EETMS, Pd/GPTMS, Pd/GO/EETMS, and Pd/GO/GPTMS, are encapsulated into mesoporous (2–10 nm) silica-alginate beads to primarily serve the development of cost-effective catalyst for on-board generation of hydrogen. Major findings involve: (i) the synthesis of porous silica alginate beads, with the controlled pore sizes (2–10 nm) as a function of concentration of alkoxysilanes, (ii) onboard release of hydrogen from the decomposition of hydrazine, which is evaluated as: (1) time-dependent disappearance of the N–N bond stretching band at 1069 cm−1 based on the FTIR spectroscopy, (2) volumetric estimation of the equimolar hydrogen using methylene blue (MB); (3) catalytic reduction of p-nitroaniline (PNA). The decomposition of high concentration of hydrazine is made possible using very low concentration of palladium. On calcination the efficiency of catalysts found to enhance further. The noteworthy finding is probing the hydrogen evolution using FTIR spectroscopy. Hydrogen selectivity of ∼100% is obtained from the most efficient catalyst (Pd/GO/EETMS-623 K).

Oxygen is known to have a significant impact on the strength of Ti alloys, whereas it can also reduce the ductility substantially. Thus, the usage of oxygen to strengthen Ti is restricted in the industry. In this study, we rekindled the research of oxygen behavior in Ti with the purpose of developing Ti alloys with high strength and suitable ductility by using no expensive and poisonous element. To this end, experiments of producing high performance commercially pure Ti using only oxygen solid solution were carried out. The oxygen element was introduced into the Ti by two different powder metallurgy methods. The microstructural examination and mechanical test were performed for the samples, which indicated a strong hardening effect of oxygen in spite of the processing routes. Most importantly, the results suggested that a high elongation to failure of over 20% can still be obtained in the samples having yield stress over 800 MPa, up to an oxygen content of 0.8 wt%, which is far beyond the previously recognized limit.

This work investigates the relative contributions to strengthening from twinning, solid-solution, precipitation, and irradiation hardening mechanisms in sputtered Cu–W thin films irradiated to different doses. A nanograin solid solution strengthening mechanism with a linear compositional dependence is observed for the as-grown alloys and for the alloy samples irradiated to 0.5 dpa. Solid solution strengthening is the major strengthening mechanism for Cu99.5W0.5 at all irradiation doses. Irradiation induces precipitation in samples with W concentrations greater than or equal to 1% at doses above ≈0.5 dpa. The growth of 1–4 nm precipitates enhances the hardness of these alloys, and the degree of strengthening is determined by the interparticle spacing. While the alloys exhibit steady-state properties after a relatively low dose (≈1 dpa), the different time scales associated with detwinning and damage accumulation in pure Cu lead transients at higher doses (>5 dpa).

The influence of hot rolling on the evolution of the interface microstructure as well as mechanical properties of the Mg/Al explosive welding composite plates was investigated. The hardening phenomenon induced by explosive welding could be eliminated effectively through preheating treatment. An intermetallic compound layer consisting of Al3Mg2 and Mg17Al12 was observed at the Mg/Al interface after annealing at 400 °C. The composite plate then was hot rolled at 400 °C with different reduction ratios. The composite plates presented different degrees of warp and edge cracks with increasing the reduction ratio. At the reduction ratio of 30%, the coordination deformation ability of the constituent Mg and Al alloys is consistent with the composite plate. The results showed that the tensile strength and the elongation of the composite plates increased significantly after hot rolling owing to the dynamic recrystallization and the intermetallic compounds thickness decrease during hot rolling.

{001} facets dominant TiO2 nanosheets have attracted intensive attention in the photocatalytic field, due to their undercoordinated Ti5c centers, higher surface energy, and photocatalytic activity than those of any other low-energy facet. However, a fluorine-rich (001) surface is controversial to the photocatalytic activity of TiO2 nanocrystals. We have removed the surface F atoms bonding with Ti by hydrogenation method successfully, and found that {001} facets dominant TiO2 nanosheets without the terminated F atoms showed dramatic enhancement in the photocatalytic activity. Moreover, the clean (001) surface was more in favor of the deposition of PdO than the fluorine-rich surface, and the amorphous structure from the hydrogenation is beneficial to the reduction of PdCl42− to Pd nanoparticles. The PdO attached on {001} facets and the amorphous structure promoted the separation of charge carriers, and Pd nanoparticles transferred plasmonic-induced electrons to the conduction band of hydrogenated TiO2 under simulated solar irradiation. Thus, a significantly enhanced photocatalytic activity of Pd–H–TiO2 is achieved on degrading organic environmental pollution, due to the synergy of palladium species and hydrogenation on {001} facets exposed TiO2.

It is desirable to evaluate the ratcheting behavior of biomedical magnesium under cyclic loading with and without precorrosion, due to the promising future in biomedical implant field. This study focuses on the investigation of the uniaxial ratcheting strain evolutions of ZEK100 magnesium alloy sheet under various loading conditions and different corrosion time. To illustrate the ratcheting response in detail, the effects of several factors on the ratcheting strain evolution were discussed, including mean stress, stress amplitude, specimen orientations, loading history, and precorroded duration. A series of asymmetrical multistep stress-controlled ratcheting tests were conducted. The mean stress, stress amplitude, and precorrosion duration have significant influence on the ratcheting response of material. ZEK100 magnesium alloy is sensitive to loading history. ZEK100 magnesium alloy exhibits anisotropic behavior, and it is found that the final ratcheting strain of transverse direction (TD) specimens is always larger than that of rolling direction (RD) specimens. The corrosion behavior of ZEK100 magnesium alloy in phosphate buffered solution (PBS) simulated physiological environment was also studied. The corrosion process is characterized by pitting corrosion, and the corrosion rate of material stabilizes at about 2.4 g/(m2 d) after an exponentially decrease at initial stage.

In the present study, the effect of heat treatment on microstructure and mechanical properties of gas tungsten arc (GTA) welded 15CDV6 high strength low alloy steel is discussed. Experiments were carried out based on Taguchi L9 orthogonal array to weld 15CDV6 plate of thickness 3.7 mm. The input parameters considered in this work were current, voltage, and welding speed. Tensile strength, microhardness, and impact strength were measured as performance characteristics. Post weld heat treatment was carried out on the weldments to study its effect on the properties of weldments and microstructures were characterized using optical microscope and the X-ray diffraction analysis revealed the presence of MO2C and VC precipitates in the weld. Post weld heat treatment of the GTA welded samples and base metal successfully produced properties required for aerospace applications.

One conceptually different approach has been developed to synthesize Ti3+ self-doped TiO2−x mesocrystals to narrow the band gap of TiO2. This simple and economical one-pot solvothermal method uses TiCl3 and tetrabutyltitanate (TBT) as a precursor and exhibits practical application. Different morphology including uniform spindle shape, tetragonal bipyramid, and capsule-like mesocrystals can be tailored easily by tuning the precursor ratio of TiCl3 to TBT. We have shown that our band gap engineered TiO2−x exhibits unique mesocrystal phase and owns substantial high visible light driven photocatalytic activities. Electron paramagnetic resonance (EPR) studies of this sample verified the presence of oxygen centered radicals, namely, hydroxyl (·OH) and superoxide radicals (O2 −·/·OOH). The catalysts have been characterized using transmission electron microscope, fluorescence spectra, Raman spectra, EPR, X-ray photoelectron spectroscopy, X-ray diffraction (XRD), Ultraviolet–visible absorption spectra, etc. It shows high catalytic stability. The findings of this work provide new insights for developing morphology tailored for visible light driven devices and other applications via controlled band gap engineering.

Porous silicon nitride ceramics are attracting extensive attention due to its high strength and low dielectric loss. However, further strength enhancement at elevated temperatures is hindered by its intergranular phase, forming from sintering additives. This paper describes the fabrication of porous silicon nitride ceramic materials, by using a replacement method of carbothermal nitridation. The initial samples which were obtained from the sintering of mixed powder consisted of 95 wt% Si3N4 and 5 wt% Y2O3. After the removal of the oxide intergranular phase and the infiltration of mixtures of phenolic resins and silica sols, carbothermal nitridation process was carried out at 1550 °C for 2 h under nitrogen. X-ray diffraction and microstructural analysis revealed a complete replacement of oxide intergranular phases by the newly formed Si3N4 intergranular phase. The unmodified ceramic exhibited lower flexural strength at 1400 °C, which was only 50% of the room-temperature strength. Although the modified ceramic attained a slightly lower flexural strength at room temperature after the replacement of intergranular phase, its strength measured at 1400 °C could attain 90% of room-temperature strength.

This work presents the effects of sintering temperature and mechanical milling on the weight loss of the powder metallurgical Fe–28Mn–3Si (wt%) alloy. Mechanically milled (MM) and blended elemental (BE) Fe–28Mn–3Si powder mixtures were prepared. Both the MM and BE compacts were sintered in a vacuum furnace for 3 h at various temperatures. It was found that weight loss occurred among all the sintered compacts. The weight loss of the sintered MM compacts was much lower than their BE counterparts sintered at the same temperature. The weight loss of the compacts was mainly caused by the sublimation of Mn in the Mn depletion region. A single α-Fe phase was observed on the surface of all the sintered samples. Predominant γ-austenite and minor ε-martensite were detected in all the sintered compacts at locations beyond the Mn depletion region. Mn3Si phase was found in BE alloys sintered at 1000 °C.

We outline the scrutiny of the two probe devices formed by placing the nonclassical fullerene molecules CM (20 ≤ M ≤ 30) within semi-infinite gold electrodes using density functional theory. The electronic structure and molecular orbitals of isolated fullerene molecules are broadened to form junction devices with charge injection at zero as well as variegated bias respectively. The molecular junctions thus formed are contemplated for two important electrical constitutions, current, and conductance. These parameters are then elaborated and contemplated for their electronic parameters namely, the density of states, transmission coefficient, molecular orbitals, molecular projected self-consistent Hamiltonian states, electron density, and Mulliken population. We conclude that C20 and C24 fullerene molecule exhibits extremely metallic behavior while others fail to demonstrate such behavior. The molecular device, thus formed, strongly supports the superconductive behavior of the C24 molecule with an ability to easily adapt by modulating its active molecular orbitals under applied potential.

We develop a phase field model for the simulation of chemical diffusion-limited solidification in complex metallic alloys. The required thermodynamic and kinetic input information is obtained from CALPHAD calculations using the commercial software-package ThermoCalc. Within the case study on the nickel-base superalloy Inconel 718, we perform simulations of solidification with the explicit consideration of 6 different chemical elements. The stationary dendritic tip velocities as functions of the constant undercooling temperature obtained from isothermal solidification are compared with the stationary tip temperatures as functions of the imposed pulling velocity obtained during directional solidification. We obtain a good quantitative agreement between the two different velocity—undercooling functions. This indicates that the model provides a self consistent description of the solidification. Finally, the simulation results are discussed in light of experimental solidification conditions found in single crystalline casting experiments of Inconel 718.

Over the years, the search for high performance thermoelectric materials has been dictated by the “phonon glass and electron crystal (PGEC)” paradigm, which suggests that low band gap semiconductors with high atomic number elements and high carrier mobility are the ideal materials to achieve high thermoelectric figure of merit. Complex oxides provide alternative mechanisms such as large density of states and strong electron correlation for high thermoelectric efficiency, albeit having low carrier mobility. Due to vast structural and chemical flexibility, they provide a fertile playground to design high efficiency thermoelectric materials. Further, developments in oxide thin film growth methods have enabled synthesis of high quality, atomically precise low dimensional structures such as heterostructures and superlattices. These materials and structures act as excellent model systems to explore nanoscale thermal and thermoelectric transport, which will not only expand the frontier of our knowledge, but also continue to enable cutting edge applications.

The metadynamic recrystallization (MDRX) behavior of a medium carbon Cr–Ni–Mo alloyed steel 34CrNiMo was investigated using two-stage hot compression test on a Gleeble thermal-mechanical simulator in the temperature range of 1273–1423 K, strain rate range of 0.1–5.0 s−1, and interval times of 0.5–5 s. The softening of the flow stress at the second stage of compression and microstructure observation confirm the occurrence of MDRX at the elevated temperatures within very short interval time. Then the MDRX softening fraction was calculated based on the flow stress curves. The results indicate that the MDRX softening fraction increased with increasing interval time, deformation temperature, and strain rate. The kinetics of MDRX softening behavior was established using Avrami equation and the apparent activation energy of MDRX for 34CrNiMo steel was evaluated as 93 kJ/mol. The predicted results show good agreements with the experimental ones, indicating the efficiency of proposed kinetics equation.

Mechanical stability of Ag and Cu printed and evaporated metallization lines on polymer substrates is investigated by means of monotonic tensile and cyclic bending tests. It is shown that lines which demonstrate good performance during monotonic tests fail at lower strains during a cyclic bending tests. Evaporated lines with the grain size of several hundreds of nanometers have good ductility and consequently good stability during monotonic loading but at the same time they fail at low strains during cyclic bending. Printed lines with nanocrystalline microstructure, in contrast, demonstrate more intensive cracking during monotonic loading but higher failure strains during cyclic bending. Apart from the grain size effect, the effect of film thickness on the saturation crack density after cyclic bending is also demonstrated. Thinner films have higher crack density in accordance with the shear lag model.