X-Ray Absorption Spectroscopy from H-Passivated Porous Si and Oxidized Si Nanocrystals

Published online by Cambridge University Press:  15 February 2011

S. Schuppler ,
S. L. Friedman ,
M. A. Marcus ,
D. L. Adler ,
Y.-H. Xie ,
F. M. Ross ,
T. D. Harris ,
W. L. Brown ,
Y. J. Chabal  and
P. J. Szajowski
...Show all authors
S. Schuppler
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
S. L. Friedman
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
M. A. Marcus
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
D. L. Adler
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
Y.-H. Xie
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
F. M. Ross
Affiliation:
National Center for Electron Microscopy, Lawrence Berkeley Laboratory, Berkeley, CA 94720
T. D. Harris
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
W. L. Brown
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
Y. J. Chabal
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
P. J. Szajowski
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
E. E. Chaban
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
L. E. Brus
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
P. H. Citrin
Affiliation:
AT&T Bell Laboratories, Murray Hill, NJ 07974
Get access

Abstract

Quantum confinement in nanoscale Si structures is widely believed to be responsible for the visible luminescence observed from anodically etched porous silicon (por-Si), but little is known about the actual size or shape of these structures. Extended x-ray absorption fine structure data from a wide variety of por-Si samples show significantly reduced average Si coordination numbers due to the sizable contribution of surface-coordinated H. (The H/Si ratios, as large as 1.2, were independently confirmed by ir-absorption and α-recoil measurements.) The Si coordinations imply very large surface/volume ratios, enabling the average Si structures to be identified as crystalline particles (not wires) whose dimensions are typically <15 Å. Comparison of the size-dependent peak luminescence energies with those of oxidized Si nanocrystals, whose shapes are known, shows remarkable agreement. Furthermore, near-edge x-ray absorption fine structure measurements of the nanocrystals shows the outer oxide and interfacial suboxide layers to be constant over a wide range of nanocrystal sizes. The combination of these results effectively rules out surface species as being responsible for the observed visible luminescence in por-Si, and strongly supports quantum confinement as the dominant mechanism occurring in Si particles which are substantially smaller than previously reported or proposed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 375: Symposia AA – Applications of Synchrotron Radiation Techniques to Materials Science , 1994 , 113
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. For example, see Mater. Res. Soc. Proc. 256 (1992); 283 (1993); 298 (1993).Google Scholar
2. Canham, L. T., Appl. Phys. Lett. 57, 1046 (1990)Google Scholar
3. Lehmann, V. and Gösele, U., Appl. Phys. Lett. 58, 856 (1991)Google Scholar
4. Schuppler, S., Friedman, S. L., Marcus, M. A., Adler, D. L., Xie, Y.-H., Ross, F. M., Harris, T. D., Brown, W. L., Chabal, Y. J., Brus, L. E., and Citrin, P. H., Phys. Rev. Lett. 72, 2648 (1994).Google Scholar
5. See, e. g., Delerue, C., Allan, G., and Lannoo, M., Phys. Rev. B 48, 11024 (1993), and references therein.Google Scholar
6. MacDowell, A. A., Hashizume, T., and Citrin, P. H., Rev. Sci. Instr. 60, 1901 (1989).Google Scholar
7. Lee, P.A., Citrin, P. H., Eisenberger, P., and Kincaid, B. M., Rev. Mod. Phys. 53, 769 (1981).Google Scholar
8. Erbil, A., Cargill, G. S., Frahm, R., and Boehme, R. F., Phys. Rev. B 37, 2450 (1988). Escape depths have been crudely estimated by multiplying by 5 to account for the 80% porosity.Google Scholar
9. Preparations of the por-Si samples studied here (referred to as A, B, C, and D) follow those in Refs. 2, 10, and 11, namely, C [2]: p-type Si(lO0), >50 Ω-cm, 20%HF in alcohol, 20 mA/cm2 for 5 min; A [11]: same as C, but etched 60 min; B [10]: p-type Si(100), >50 (Ω-cm, 15%HF in alcohol, 25 mA/cm2 for 12 min; D [11]: p-type Si(100), 0.5–0.8 Ω-cm, 40% HF in alcohol, 50 mA/cm2 for 80 sec, soaked 2 hr unetched in same solution.50+Ω-cm,+20%HF+in+alcohol,+20+mA/cm2+for+5+min;+A+[11]:+same+as+C,+but+etched+60+min;+B+[10]:+p-type+Si(100),+>50+(Ω-cm,+15%HF+in+alcohol,+25+mA/cm2+for+12+min;+D+[11]:+p-type+Si(100),+0.5–0.8+Ω-cm,+40%+HF+in+alcohol,+50+mA/cm2+for+80+sec,+soaked+2+hr+unetched+in+same+solution.>Google Scholar
10. Friedman, S. L., Marcus, M. A., Adler, D. L., Xie, Y.-H., Harris, T. D., and Citrin, P. H., Appl. Phys. Lett. 62, 1934 (1993).Google Scholar
11. Xie, Y. H., Hybertsen, M. S., Wilson, W. L., Ipri, S. A., Carver, G. E., Brown, W. L., Dons, E., Weir, B. E., R.Kortan, A., Watson, G. P., and Liddle, A. J., Phys. Rev. B 49, 5386 (1994); Y.-H. Xie (unpublished).Google Scholar
12. Oxidized Si nanocrystals were made by homogeneous nucleation in high-pressure He at 1000°C from thermal decomposition of disilane with subsequent oxidation in O2 at 1000°C for ∼30 msec. See K. A. Littau, Szajowski, P. J., Muller, A. J., Kortan, A. R., and Brus, L. E., J. Phys. Chem. 97, 122 (1993); W. L. Wilson, P. J. Szajowski, and L. E. Brus, Science 262, 1242 (1993); P. J. Szajowski and L. E. Brus (unpublished).Google Scholar
13. Like the nanocrystals, the por-Si sample also consists of small particles whose band structure is not fully developed, and therefore exhibits neither the larger white-line to edge-jump ratio nor the split white-line structure of c-Si. Our results are completely unaffected by this choice because only difference spectra are being compared.Google Scholar
14. Densities and molecular weights for bulk c-Si, SiO2, and SiO were used, i. e., 2.33, 2.4, and 2.1 gm cm−3, respectively.Google Scholar
15. It should be noted that while the outer diameters of the nanocrystals, determined by TEM in Ref. 12, have very conservative error limits of ≤20 %, the relative mass fractions, determined by NEXAFS, are much more precise. Thus, the relative error limits of the inner diameters and the oxide layer thicknesses are just the same as for the outer diameters.Google Scholar
16. Brus, L. E., Szajowski, P. F., Wilson, W. L., Harris, T. D., Schuppler, S., and Citrin, P. H., J. Amer. Chem. Soc. (to be published).Google Scholar
17. Street, R. A., Hydrogenated Amorphous Silicon (Cambridge University Press, Cambridge, 1991).Google Scholar
18. The volumes used for integrating the measured SiHx concentrations in the por-Si samples were obtained from TEM.Google Scholar
19. Surface sensitivity of <1 μm was obtained using a grazing internal incidence angle in a Ge plate positioned next to the por-Si samples.Google Scholar
20. For a Si cube of side L, Nsi = 8L 3 /a 0 3; for a sphere of diameter L, Nsi= (π/ 6 )NSi cube.Google Scholar