Bulk samples of a novel cermet (ceramic/metal composite) hydrogen transport membrane (HTM) were subjected to thermal cycling in the temperature range between 25-850°C to study phase transformations and microstructural changes under thermal shock. Scanning electron microscopy (SEM) and electron probe micro analyzer (EPMA) with energy dispersive spectroscopy (EDS) were used to characterize the microstructural and chemical changes in the membrane upon thermal cycling. SEM & EPMA analyses indicated that the temperature gradient during thermal cycling produced more micro-cracks inside the HTM disc, whereas, the chemical reaction between Pd and oxygen to form PdO disturbed the continuity of the metal palladium (Pd) - Yttria Stabilized Zirconia (YSZ) dual phases interconnection system from surface down. The agglomerates of un-crystallized YSZ grains found to be the inherent in the cracks of the as-received HTM. A combination of trans-granular and inter-granular crack propagation results around the YSZ grains and the new precipitates. Based on the electron fractography analyses by both SEM and EPMA, the micro voids coalescence develops ahead of the crack tips in the cross-section of the HTM after 500 thermal cycles.
To send this article to your Kindle, first ensure no-reply@cambridge.org is added to your Approved Personal Document E-mail List under your Personal Document Settings on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part of your Kindle email address below. Find out more about sending to your Kindle. Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations. ‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi. ‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
Find out more about the Kindle Personal Document Service.
To save this article to your Dropbox account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Dropbox account. Find out more about saving content to Dropbox.
To save this article to your Google Drive account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Google Drive account. Find out more about saving content to Google Drive.