Nature of Slip in γ-Titanium Aluminide Above the Yield Stress Anomaly Temperature

Published online by Cambridge University Press:  10 February 2011

S. Jiao ,
N. Bird ,
P. B. Hirsch  and
G. Taylor
S. Jiao
Affiliation:
University of Oxford, Department of Materials, Parks Road, Oxford, OXI 3PH, UK
N. Bird
Affiliation:
University of Oxford, Department of Materials, Parks Road, Oxford, OXI 3PH, UK
P. B. Hirsch
Affiliation:
University of Oxford, Department of Materials, Parks Road, Oxford, OXI 3PH, UK
G. Taylor
Affiliation:
University of Oxford, Department of Materials, Parks Road, Oxford, OXI 3PH, UK
Get access

Abstract

Crystals of γ-TiAl, containing ∼54.5 at% Al, with various orientations were deformed at different temperatures and examined by transmission electron microscopy (TEM). It was found that while in many cases slip and climb of ordinary dislocations tend to predominate, slip by [001] dislocations can be important also. The occurrence of [001] slip has not been reported before. The values of critical resolved shear stress were determined and strong locks on [001] dislocations have been identified as local segments of ½ ⟨112] dislocations arising from interactions between [001] and ½⟨110] dislocations.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 552: Symposium KK – High-Temperature Ordered Intermetallic Alloys VIII , 1998 , KK8.12.1
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Kawabata, T., Kanai, T. and Izumi, O., Acta Metall. 33, 1355 (1985).CrossRefGoogle Scholar
2. Bird, N., Taylor, G. and Sun, Y.Q. in High Temperature Ordered Intermetallic Alloys, VI, edited by Horton, J., Baker, I., Hanada, S., Noebe, R.D. and Schwartz, D.S. (Mater. Res. Soc. Proc. 364, Pittsburgh, PA, 1995) pp. 635–640.Google Scholar
3. Inui, H., Matsumuro, M., Wu, D-H. and Yamaguchi, M., Phil. Mag. A, 75, 395 (1997).CrossRefGoogle Scholar
4. Jiao, S., Bird, N., Hirsch, P.B. and Taylor, G., Phil. Mag. A, 78, 777.CrossRefGoogle Scholar
5. Jiao, S., Bird, N., Hirsch, P.B. and Taylor, G., this conference.Google Scholar
6. Bird, N., D.Phil. thesis, Oxford University.Google Scholar