Interfacial Shear Strength of Thin Polymeric Coatings on Glass

Published online by Cambridge University Press:  22 February 2011

J. E. Ritter ,
L. Rosenfeld ,
M. R. Lin  and
T. J. Lardner
J. E. Ritter
Affiliation:
Mechanical Engineering Department, University of Massachusetts, Amherst, MA 01003
L. Rosenfeld
Affiliation:
Mechanical Engineering Department, University of Massachusetts, Amherst, MA 01003
M. R. Lin
Affiliation:
Mechanical Engineering Department, University of Massachusetts, Amherst, MA 01003
T. J. Lardner
Affiliation:
Mechanical Engineering Department, University of Massachusetts, Amherst, MA 01003
Get access

Abstract

The interfacial adhesive shear strengths of epoxy and acrylate coatings on glass substrates were measured by the indentation and lap shear tests. The lap shear strengths were about an order of magnitude less and exhibited considerably more variability than those measured by indentation. It is believed that the lap shear strength is controlled by large processing flaws (pores in this study); whereas, the indentation test measures the “intrinsic” strength of the coating.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 130: Symposium C – Thin Films: Stresses and Mechanical Properties I , 1988 , 237
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

1. Kinloch, A. J., J. Mat. Sci., 17, 617–651 (1982).10.1007/BF00540361CrossRefGoogle Scholar
2. Mittal, K. L. (Ed.), Adhesion Measurements on Thin Coating, Thick Coating and Bulk Coatings, ASTM STP 640, American Society for Testing and Materials, Philadelphia (1968).Google Scholar
3. Gent, A. N., J. Adhesion, 23, 115–122 (1987).CrossRefGoogle Scholar
4. Wu, Souheng, Polymer Interface and Adhesion, (Marcel Dekker, Inc., New York 1982) p. .Google Scholar
5. Mittal, K. L., J. Adhesion Sci. Tech., 1 (3), 247–59 (1987).CrossRefGoogle Scholar
6. Ritter, J. E., Lardner, T. J., Rosenfeld, L., and Lin, M., submitted for publication (1988).Google Scholar
7. Ritter, J. E., Rosenfeld, L., Lin, M. R., and Lardner, T. J., submitted for publication (1988).Google Scholar
8. Matthewson, M. J., Appl. Phys. Lett., 49 (21), 1426–28 (1986).CrossRefGoogle Scholar
9. Weibull, W. A., J. Appl. Mech., 18, 239–97 (1951).CrossRefGoogle Scholar
10. Davies, D. G. S., Proc. Brit. Ceram. Soc., 22, 429–52 (1973).Google Scholar