Published online by Cambridge University Press: 17 March 2011
The quasicrystalline phase forming ability, solidification structure, thermal stability, and phase relationships of a series of conventionally-cast Al62-xCu25.5Fe12.5Bex (x=0,1,3,5,7) alloys were investigated. Single icosahedral quasicrystalline phase was successfully obtained by partial replacement of Al with Be (7 at.%) in an Al62Cu25.5Fe12.5 alloy during crucible cooling. The I-phase in an Al55Cu25.5Fe12.5Be7 alloy has the same face-centered icosahedral structure as that in an Al62Cu25.5Fe12.5 alloy, with less phason strain. Hardness of the I-phase increases with x, i.e. from Hv 710 for x=1 to Hv 809 for x=7.