The Effect of H2 Dilution on the Stability of a-Si:H based Solar Cells

Published online by Cambridge University Press:  16 February 2011

Liyou Yang  and
Liang-Fan Chen
Liyou Yang
Affiliation:
Solarex Corporation, Thin Film Division, 826 Newtown-Yardley Road, Newtown, PA 18940
Liang-Fan Chen
Affiliation:
Solarex Corporation, Thin Film Division, 826 Newtown-Yardley Road, Newtown, PA 18940
Get access

Abstract

We have systematically investigated the effect of H2 dilution on the stability of a-Si:H based solar cells. The results clearly show that the device stability against light soaking improves substantially with increasing H2 dilution until a threshold is reached. Beyond this threshold which depends on the substrate temperature, the stability no longer changes with further increase in H2 dilution. On the other hand, at a given ratio of H2 to the reactant gases, the device stability generally improves with increasing substrate temperature. Multi-step light soaking experiments have shown that devices made with H2 dilution saturate much faster (∼100 hours) under one-sun illumination and exhibit little overshoot effect in the recovery process, in sharp contrast to devices made without H2 dilution. Based on the simple two-component model for defect kinetics, these observations and the fact that the apparent saturation time coincides with the time constant of the “fast” defects strongly suggest that negligible amount of “slow” defects exist in materials made with H2 dilution. While H2 dilution generally suppresses the formation of microstructure giving rise to dihydride bonding and microvoids, the differences in the kinetics of light induced degradation cannot always be traced to obvious differences in these structural properties.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 336: Symposium A – Amorphous Silicon Technology - 1994 , 1994 , 669
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Yang, L., Chen, L., and Catalano, A., Appl. Phys. Lett. 59, 840 (1991).Google Scholar
2. Yang, L. and Chen, L., J. Non-Cryst. Solids 137&138, 11 89 (1991).Google Scholar
3. Chen, L. and Yang, L., J. Non-Cryst. Solids 137&138, 1185 (1991).Google Scholar
4. Yang, L., Chen, L., Hou, J. and Li, Y-M., MRS Symp. Proc. Vol. 258, 365 (1992).Google Scholar
5. Yang, L. and Chen, L., Appl Phys. Lett. 63, 400 (1993).Google Scholar
6. Stutzmann, M., Jackson, W., and Tsai, C.C., Phys. Rev. B 32, 23 (1985).Google Scholar
7. Redfield, D. and Bube, R.H., Appl. Phys. Lett. 54, 1037 (1989).CrossRefGoogle Scholar
8. Bennett, M., Rajan, K. and Kritikson, K., in Conf. Record of the 23rd IEEE Photovoltaic Specialist Conf. (Louisville, KY, 1993) p. 790.Google Scholar
9. Bennett, M.S. and Rajan, K., in Conf. Record of the 20th IEEE Photovoltaic Specialist Conf. (Las Vegas, Nevada 1988) p. 67.Google Scholar
10. Yang, L., Chen, L. and Catalano, A., MRS Symp. Proc. Vol. 219, 259 (1991).Google Scholar
11. Mahan, A.H., Williamson, D.L., Nelson, B.P., and Crandall, R.S., Phys. Rev. B 40, 12024 (1989).CrossRefGoogle Scholar
12. Xu, X., Yang, J. and Guha, S., MRS Symp. Proc. Vol. 297, 649 (1993).Google Scholar
13. Williamson, D.L. (private communication).Google Scholar