A Cross-Sectional TEM Study of the Effects of Annealing Conditions on the Regrowth of Lead-Implanted Single Crystal Calcium Titanate

Published online by Cambridge University Press:  26 February 2011

J. Rankin ,
L. A. Boatner ,
C. W. White  and
L. W. Hobbs
J. Rankin
Affiliation:
Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, MA 02139
L. A. Boatner
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831.
C. W. White
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831.
L. W. Hobbs
Affiliation:
Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, MA 02139
Get access

Abstract

The atmospheric effects of oxygen and water vapor on the epitaxial regrowth behavior of ion-implanted CaTiO3 have been studied. Cross-sectional transmission electry microsgopy (TEM) samples prepared from crystals implanted with 1(1015) Pb/cm2 at 540 KeV, were annealed at 450–650°C for 40 – 80 minutes, in environments containing different percentages of oxygen and water vapor. Regrowth was studied for implantation directions along both the <010> and <100> crystallographic directions of this orthorhombic Perovskite structure, space group Pcmn. TEM on unannealed crystals indicated the presence of an amorphous region extending approximately 190 nm in from the edge of the sample as a result of ion-implantation. Annealing produced an epitaxial regrowth of the amorphous region. The regrowth process began at the original amorphous/crystalline interface and proceeded outward to the surface of the sample. It was found that the epitaxial regrowth rate increased as the amount of water vapor in the annealing atmosphere was increased. In addition, it was observed that the amount of oxygen present during annealing did not alter the rate of recrystallization in this system.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 100: Symposium – A Fundamentals of Beam-Solid Interactions and Transient Thermal Processing , 1988 , 453
Copyright
Copyright © Materials Research Society 1988

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Rankin, J., Hobbs, L.W., Boatner, L.A., White, C.W., To be published in the Proceedings of Radiation Effects in Insulators -4 Conf., 6–10 July 1987, Lyon, France.Google Scholar
2. White, C.W., Boatner, L.A., Sklad, P.S., McHargue, C.J., Rankin, J., Farlow, G.C., Aziz, M.J., To be published in the Proceedings of Radiation Effects in Insulators -4 Conf., 6–10 July 1987, Lyon, France.Google Scholar
3. Ohkubo, M., Hioki, T., Kawamoto, J., J. Appl. Phys. 60(4), 15 August 1986, 1325.Google Scholar
4. Cartz, L., Karioris, F.G., Fournelle, R.A., Appaji Gowda, K., Ramasami, K., Sarkar, G., Billy, M., Rad. Eff., 54, 1981, 57.Google Scholar
5. Williams, J.S., Nucl. Inst. and Meth. 209/208(1983) 219.Google Scholar
6. Spaepen, F., Turnbull, D., AlP Conf. Ser. 50 (1979) 73.Google Scholar
7. Greegor, R.B., Lytle, F.W., Ewing, R.C., Haaker, R.F., Nucl Instr. and Meth. B1, 1984, 587.Google Scholar
8. Whittemore, O.J., Varela, J.A., Advances in Ceramics - Vol 10, Structure and Properties of MgO and Al2O3 Kingery, W.D. ed., 1984, 583.Google Scholar
9. Fratello, V.J., Hays, J.F., Turnbull, D., J. Appl. Phys. 51(9), 1980, 4718.CrossRefGoogle Scholar
10. Leko, V.K., Komarova, L.A., Inorg. Matls. (trans), 11, 1975, 1597.Google Scholar