Nanoporous Alumina Films Prepared from Colloidal Solution

Published online by Cambridge University Press:  21 February 2011

Vladimir Petrovsky ,
Harlan U. Anderson  and
Tatiana Petrovsky
Vladimir Petrovsky
Affiliation:
EMARC, University Missouri-Rolla, MO 65401.
Harlan U. Anderson
Affiliation:
EMARC, University Missouri-Rolla, MO 65401.
Tatiana Petrovsky
Affiliation:
EMARC, University Missouri-Rolla, MO 65401.
Get access

Abstract

Alumina layers were deposited by spin coating and dip coating on different substrates (Pt, Si, Al2O3) from the water suspension of nanosize boehmite particles. It was shown, that addition of the butoxyethanol in the suspension improves wetting and the quality of the film. No separation from the substrate or cracking of the film took place up to 1000°C on all types of the substrates for the film thickness up to 10μm. Because of the minimal shrinkage, the coating can be used to smooth rough substrates as well as provide interfacial layers for either single layer or multilayer structures.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 581: Symposium F – Nanophase & Nanocomposite Materials II , 1999 , 553
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Yoldas, B.E., Am. Ceram.Soc. Bull., 54 [3], pp.289–90 (1975).Google Scholar
2. Yoldas, B.E., J. Amer. Chem. Biotechnol., 23 [11], pp. 803–9 (1975).Google Scholar
3. Lin, Yue-Sheng, and Anthonie Burggraaf, J., J.Am.Ceram.Soc., 74 [1], pp.219–24 (1991).Google Scholar
4. Uhlhorn, R.J.R., Huisintvelt, M.H.B.J., Keizer, K., and Burggraaf, A.J., J.Mater.Sci, 27, pp.527–37 (1992).Google Scholar
5. Drabarek, E., Finnie, K.S., Bartlett, J.R., Woolfrey, J.L., Mitchell, D. in Sol-Gel Processing of Advanced Materials, edited by Lisa Klein, C., Pope, Edward J.A., Sakka, Simo, Woolfrey, James L. (Am.Ceram.Soc., 81, Westerville, Ohio 1998).Google Scholar
6. Shaw, Leon, and Abbaschian, Reza, J.Am.Ceram.Soc., 78 [12], pp.3376–82 (1995).Google Scholar
7. Brinker, C.J., and Scherer, G.W., Sol-Gel Science. The Physics and Chemestry of Sol-Gel Processing, Academic Press, San Diego, CA, 1990.Google Scholar
8. Brinker, C.J., Hurd, A.J., Frye, G.C., Ward, K.J., and Ashly, C.S., J.Non-Cryst.Solids, 121, p.294 (1990).Google Scholar
9. Vorotilov, K., Petrovsky, V., and Vasiljev, V., J.Sol-Gel Sci. & Technol., 5, pp. 173–83 (1995).Google Scholar