Stress and current induced degradation of the interconnects may well define the ultimate limits on device density and total on-chip power in microelectronic circuits. The two damage mechanisms are found to be mutually interdependent in a fashion determined by the line microstructure, as well as by design features such as W-studs and refractory metal back up layers. We have developed a comprehensive model for the synergistic effects of stress migration and electromigration, taking such factors into account. The present work reviews the modelling of the statistical failure distributions, with emphasis on the temperature and current density dependencies, for the case of 'near-bamboo' sub-micron lines.
To send this article to your Kindle, first ensure no-reply@cambridge.org is added to your Approved Personal Document E-mail List under your Personal Document Settings on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part of your Kindle email address below. Find out more about sending to your Kindle. Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations. ‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi. ‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
Find out more about the Kindle Personal Document Service.
To save this article to your Dropbox account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Dropbox account. Find out more about saving content to Dropbox.
To save this article to your Google Drive account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Google Drive account. Find out more about saving content to Google Drive.