Microstructure and Mechanical Properties of Ll2-Structure Alloys Based on Al3Zr

Published online by Cambridge University Press:  26 February 2011

J. H. Schneibel  and
W. D. Porter
J. H. Schneibel
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P. O. Box 2008, Oak Ridge, TN 37831
W. D. Porter
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P. O. Box 2008, Oak Ridge, TN 37831
Get access

Abstract

The tetragonal compound Al3Zr can be transformed into the cubic Ll2 structure by additions of Cr, Fe, Ni or Cu. This result is interpreted in terms of Pettifor's structure map. The transformation is accompanied by substantial softening. The significant porosity of cast buttons which develops during the homogenization required to produce the Ll2 structure is attributed to the Kirkendall effect. Al-5.5Fe-25Zr (at. %) specimens with the Ll2 structure can be deformed at room temperature in compression, and their yield stress has been determined as a function of temperature. Al-Fe-Zr is nevertheless a brittle material. This is illustrated for Al-Fe-V-Zr Ll2-structure compound, the fracture toughness of which is only slightly higher than that of sintered SiC. Evidence is presented to suggest that Ll2 formation is accompanied by an increase in toughness. Significant improvements in the mechanical properties of Al3Zr-type alloys may possibly be achieved by improved processing.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 133: Symposium H – High-Temperature Ordered Intermetallic Alloys III , 1988 , 335
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Liu, C. T., White, C. L. and Horton, J. A., Acta Metall. 33, 213 (1985).CrossRefGoogle Scholar
2. Proceedings of the Materials Research Society Symposium on High-Temperature Ordered Intermetallic Compounds, edited by Koch, C. C., Liu, C. T. and Stoloff, N. S. (Materials Research Society, Pittsburgh, PA, 1985), Vol.39.Google Scholar
3. Proceedings of the Materials Research Society Symposium on High-Temperature Ordered Intermetallic Alloys II, edited by Stoloff, N. S., Koch, C. C., Liu, C. T. and Izumi, O. (Materials Research Society, Pittsburgh, PA, 1987), Vol.81.Google Scholar
4. Nose, T. and Fujii, T., J. Amer. Ceram. Soc. 71, 328 (1988).Google Scholar
5. Tada, H., Paris, P. C. and Irwin, G. R., “The Stress Analysis of Cracks Handbook,” 2nd edition, Paris Production Inc. (and Del Research Corporation), St. Louis, MO, 1985.Google Scholar
6. Raman, A. and Schubert, K., Z. Metallkde. 56, 99 (1965).Google Scholar
7. Pettifor, D. G., New Sci., No. 5, 48 (1986).Google Scholar
8. Pettifor, D. G., J. Phys. C 19, 285 (1986).CrossRefGoogle Scholar
9. Villars, P. and Calvert, L. D., Pearsons Handbook of Crystallographic Data for Intermetallic Phases, American Society for Metals, Metals Park, OH, 1985, Vol. I, p. 707.Google Scholar
10. Kumar, K. S. and Pickens, J. R., Scr. Metall. 22, 1015 (1988).Google Scholar
11. Schneibel, J. H., Becher, P. F. and Horton, J. A., J. Mater. Res. 3, 1272 (1988).CrossRefGoogle Scholar