Defect Cluster Structure and Tensile Properties of Copper Single Crystals Irradiated With 600 MeV Protons

Published online by Cambridge University Press:  15 February 2011

Yong Dai  and
Max Victoria
Yong Dai
Affiliation:
Paul Scherrer Institute, 5232 Villigen PSI, Switzerland
Max Victoria
Affiliation:
CRPP-Ecole Polytechnique de Lausanne, Fusion Technology Materials, 5232 Villigen PSI, Switzerland
Get access

Abstract

The defect microstructures and tensile properties of high purity copper single crystals have been studied after irradiation at room temperature with 600 MeV protons in the dose range from 10-3 to 10-1 dpa. The defect number density N of clusters shows a linear dependence with dose up to a saturation value of 4×1023 m-3, with a broad transition region between doses of 3×10-3 and 10-1 dpa. The increase in critical resolved shear stress (CRSS) induced by the irradiation is proportional to the square root of the dose, up to a dose of 7×10-3 dpa. These results are compared to those of both fission and fusion neutron irradiations, showing that in room temperature irradiations at low fluences, no recoil spectra effects can be detected.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 439: Symposium B – Microstructure Evolution During Irradiation , 1996 , 319
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

1. Stathopuolos, A.Y., Phil. Mag 44, 285 (1981) and A.Y. Stathopuolos, C.A. English. B.L. Eyre and P.B. Hirsh, Phil. Mag 44, 309 (1981).Google Scholar
2. Yoshida, N., Akashi, Y., Kitajima, K. and Kiritani, M., J. Nucl. Mater. 133–134, 405 (1985)Google Scholar
3. Zinkle, S.J., J. Nucl. Mater. 150, 140 (1987).Google Scholar
4. Satoh, Y., Ishida, I., Yoshiie, T. and Kiritani, M., J. Nucl. Mater. 155–157, 443 (1988).Google Scholar
5. Horsewell, A., Singh, B.N., Proennecke, S., Sommer, W.F. and Heinisch, H.L., J. Nucl. Mater. 179–181, 924 (1991).Google Scholar
6. Muroga, T., Heisch, H.L., Sommer, W.F. and Ferguson, P.D., J. Nucl. Mater. 191–194, 1150 (1992).Google Scholar
7. Zinkle, S.J., Horsewell, A., Singh, B.N. and Sommer, W.F., J. Nucl. Mater. 212–215, 132 (1994).Google Scholar
8. Makin, M.J., Whapham, A.D. and Minter, F.J., Phil Mag. 7, 285 (1962).Google Scholar
9. Rühle, M., Phys. Stat. Sol. 19, 263, 279 (1967).Google Scholar
10. Blewitt, T.H., Coltman, R.R., Jamison, R.E. and Redman, J.K., J. Nucl. Mater 2, 277 (1960).Google Scholar
11. Fischer, J., Z. Naturforsch. 17A, 603 (1962).Google Scholar
12. Koppenaal, T.J., Acta Met. 12, 487 (1964) and J. Appl. Phys. 35, 2750 (1964).Google Scholar
13. Diehl, J., Radiation Damage in Solids, (IAEA, Vienna, 1962), Vol.1, p 129.Google Scholar
14. Diehl, J. and Schilling, W., Third Intern. Conf. on Peaceful Uses of Atomic Energy, (IAEA, Vienna, 1965), p. 72.Google Scholar
15. Makin, M.J., Proc. Metall. Society Conf., vol.37, Radiation Effects, ed. Sheely, W.F., 627(1965).Google Scholar
16. Shinohara, K. and Kitajima, S., J. Nucl. Mater 133–134, 690 (1985).Google Scholar
17. Heinisch, H. L. and Martinez, C.J., J. Nucl. Mater 141–143, 886 (1986).Google Scholar
18. Heinisch, H. L., J. Nucl. Mater 155–157, 121 (1988).Google Scholar
19. Heinisch, H. L., Hamilton, M.L., Sommer, W.F. and Ferguson, P.D., J. Nucl. Mater 191–194, 1177 (1992).Google Scholar
20 Marmy, P., Daum, M., Gavillet, D., Green, S., Green, W.V., Hegedus, F., Proennecke, S., Rohre, U., Stiefel, U. and Victoria, M., Nucl. Instr. and Meth. B47, 37 (1990).Google Scholar
21 Proennecke, S., PhD Thesis No. 1067, Ecole Polytechnique de Lausanne, Switzerland, (1992)Google Scholar
22. Susuki, H., Ikeda, S. and Takeuchi, S., J.Phys. Soc. Japan 11, 382 (1956).Google Scholar
23. Singh, B.N. and Zinkle, S.J., J. Nucl. Mater. 206, 212 (1993).Google Scholar
24. Hirsch, P.B., in Vacancies 76, ed. by Smallman, R.E. and Harris, J.E. (The Metals Society, 1976), p. 95.Google Scholar
25. Neuhiuser, H., in Dislocations in Solids, ed. Nabarro, F.R.N., vol.6, 319 (1983).Google Scholar