A novel surface modification technique for aluminum

Published online by Cambridge University Press:  03 March 2011

R.S. Timsit  and
D.C. Lauzon
R.S. Timsit
Affiliation:
Alcan International Ltd., Kingston R & D Centre, P.O. Box 8400, Kingston, Ontario, Canada K7L 5L9
D.C. Lauzon
Affiliation:
Alcan International Ltd., Kingston R & D Centre, P.O. Box 8400, Kingston, Ontario, Canada K7L 5L9
Get access

Abstract

Surface modification is achieved by coating the aluminum surface with a powder mix of {Si + flux + a metal (Me)} and heating at ∼600 °C for a time interval of the order of 1 min. During heating, the flux melts and dissolves the native surface oxide film on aluminum, thus allowing Si to react with the substrate to form a film of liquid Al-Si alloy of near-eutectic composition. The component Me of the powder coating then reacts with the molten metal layer to modify the metallurgical properties of the surface after solidification.

Information

Type
Rapid Communications
Information
Journal of Materials Research , Volume 9 , Issue 3 , March 1994 , pp. 531 - 534
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1Timsit, R. S., U.S. Patent No. 5 100048, March 31 (1992).Google Scholar
2Timsit, R. S. and Janeway, B. J., J. Mater. Res. 8, 2749 (1993).Google Scholar
3Timsit, R. S., U.S. Patent No. 5 190596, March 2 (1993).Google Scholar
4Thompson, W. T. and Goad, D.G.W., Can. J. Chem. 154, 3342 (1976).CrossRefGoogle Scholar
5Wallace, E. R. and Dewing, E. W., U.S. Patent No. 3 951328, April 20 (1976).Google Scholar
6Timsit, R. S. and Lauzon, D. C., unpublished.Google Scholar
7Binary Alloy Phase Diagrams, edited by Massalski, T. B. (ASM INTERNATIONAL, Materials Park, OH, 1990).Google Scholar
8Ternary Alloys, edited by Petzow, G. and Effenberg, G. (ASM INTERNATIONAL, Materials Park, OH, 1992), Vol. 5.Google Scholar
9Timsit, R. S., Stratford, G., and Fairlie, M., Tribology and Mechanics of Magnetic Storage Systems, STLE Special Pub. SP-22 4, 98 (1987).Google Scholar