Published online by Cambridge University Press: 31 January 2011
A novel approach has been used to develop (100) faceted diamond films with flat, smooth surfaces. A morphological study of the early stages of growth behavior of (100) homoepitaxial films versus process temperature and methane percentage was carried out using atomic force microscopy. The results showed that spiral growth features and penetration twin density were dominant for growth conditions not well suited for (100) growth. Optimized process parameters were found to proceed via a step mechanism consistent with ledge growth on (2 × 1) reconstructed (100) diamond surfaces. These optimized conditions were then applied to growth of polycrystalline diamond on pretreated silicon substrates. A unique octahedral faceted film resulted, indicating strong preference for growth in the 〈100〉 direction. Scanning electron microscopy, x-ray diffraction, and Raman spectroscopy were used to assess film morphology, internal fiber texture, and carbon phase, respectively. A second stage growth step was used to flatten the surface topography to achieve the desired (100) flat tile-like morphology. This smooth (100) surface exhibited enhanced tribological performance compared to a typical randomly textured diamond film.
To send this article to your Kindle, first ensure no-reply@cambridge.org is added to your Approved Personal Document E-mail List under your Personal Document Settings on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part of your Kindle email address below. Find out more about sending to your Kindle. Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations. ‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi. ‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
Find out more about the Kindle Personal Document Service.
To save this article to your Dropbox account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Dropbox account. Find out more about saving content to Dropbox.
To save this article to your Google Drive account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Google Drive account. Find out more about saving content to Google Drive.